In reinforced concrete structure, the crack width of cold wire drawing is smaller than that of circular steel bar or even that of hot rolled thread bar. So cold wire drawing is more popular in the construction industry. The material for cold drawing is made of steel bars and can be simply explained how it is made, that is, its production process is simple. It’s based on steel bars, which are constantly stretched evenly, stretching the bars into something very thin, like wire drawing, without plasticity.

Hot dip galvanizing is then oiled and chromed. The quality of hot-galvanized sheet produced by this method is significantly improved compared with that by wet galvanizing method. It is only valuable for small-scale production. Continuous galvanizing production line includes a series of pretreatment procedures, such as alkali degreasing, hydrochloric acid pickling, water washing, solvent coating, drying, etc., and the original plate needs to be annealed in cover furnace before entering the galvanizing line.

Iron wire rust is a headache, not only the product performance decline, affect the use effect and life, and rust to human body and the environment also has a certain harm. Galvanized iron wire compared with ordinary iron wire more than a galvanized process, galvanized iron wire can rust?

Compared with other galvanizing processes, galvanized steel wire has low cleaning requirements before plating. However, under the current trend of increasing the quality level of galvanized layer, some pollutants brought into the plating tank are obviously harmful. Because cleaning galvanized coating wastes a lot of time and reduces production, it is very important to properly clean and effectively rinse the substrate before electroplating.

Wire mesh production of general selection of low carbon wire, after fine and accurate active welding equipment processing, the selection of galvanized process surface treatment. After the completion of the product, the net surface is smooth and regular, good integrity, strong and consolidated, even if part of the choice or pressure will not appear lax phenomenon.

With the development of mining industry, pig iron classification in Our country has been very extensive, to meet the needs of the machinery industry. Generally speaking, iron wire factory produces galvanized iron wire iron can be divided into two categories, is directly from the iron ore through iron tracing exercise out of the metal, the primary components of the ore is iron oxide, silica and other miscellaneous stones. When this ore is specially refined into metal iron, the elements such as carbon, silicon, manganese and so on are mixed in, so that the refined data is called – like general pig iron, also for the initial grade of the material.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.