Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

4. Keep the rinse water clean after pickling the steel wire

We must have a certain understanding of the hexagonal network, we are the beautiful appearance of the hexagonal network, hexagonal network is not only very beautiful appearance, in fact, the practical value of survival is very high. To introduce the relevant information should be very clearly know the highway guardrail net, hexagonal wire netting in all kinds of fence netting, in the value of the high-speed on the road more MaoJian, it not only be used in all kinds of road, in a sports ball games venue and try our best to take care of landslides, also has reached very matter effectiveness.

Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.

Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.

Now many industrial products will be made of stainless steel wire rope material. In order to identify the fake and inferior stainless steel, certain measures and methods can be taken. But many customers do not know what way to identify, listed the following identification methods for you.

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.