Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

There are still some differences between electric mesh and wire mesh and steel mesh. This mesh is mainly a welding mesh made of high quality low carbon steel wire after straightening and cutting, and then welded by electric welding equipment. It can be said that because of the characteristics of fast production and convenient transportation, it has been applied in many industries. In today’s construction projects, people can also see the image of this network well. The application of welded mesh in this industry is mentioned because of its strong corrosion resistance and uniform mesh. It has become a special grid for floor heating in construction industry and has been applied in many fields.

The production of large rolls of galvanized wire iron can be divided into two categories, is directly from the iron ore after iron stroke exercise out of the metal, the composition of the ore is iron oxide, silica and other miscellaneous stone.

Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

1. Adjust electroplating process parameters

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

Hexagonal mesh is made of galvanized iron wire woven by automatic mesh machine, mesh into regular hexagonal, mesh standard, beautiful, mesh size can be customized according to customer requirements, usually 27mm,20mm, 13mm, wire diameter from 0.40mm to 1.20mm, to meet the requirements of different customers.