Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

That said, it can always deform by pulling hard without changing its integrity, so cold drawing has usually reached a limit, which is not a problem, because without this property it increases hardness, which is the desired effect. Cold wire drawing encountered more rain, when the climate is wet, easy oxidation and rust. Therefore, in the storage process should pay attention to avoid rust.

In order to make the zinc content of steel wire stable in the future, and maintain its uniformity, as far as possible to reduce the zinc content, and effectively reduce zinc consumption to the actual work, the following measures are proposed by the wire factory:

When galvanized wire is galvanized, it is generally necessary to pay attention to the following problems: the duration of the protective effect of galvanized wire is greatly related to the thickness of the coating. Generally speaking, in the dry main gas and in indoor use, the thickness of galvanized wire galvanized layer only 6-12 μm “, and in harsh environmental conditions, galvanized wire galvanized layer thickness needs 20μm “to B height up to 50μm”. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire.

With the opening of metro in large and medium-sized cities, as well as the vigorous promotion of subway service in network tools, those who have been accustomed to the subway as a daily means of transportation and urban traffic. These citizens, who love the subway, rely on it and enjoy its speed, often like to call themselves the U-pin price. Is widely used in industry, agriculture, farming, construction, transportation and other welded wire mesh is used in the field of high quality low carbon wire line of welding and become, then after cold, hot dip plating, PVC plastic coated surface passivation, such as plasticizing processing, production of metal mesh with smooth surface, uniform mesh, solder joint is firm, stability, corrosion resistance, good corrosion resistance characteristics.

Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.

Hexagonal mesh is based on wire mesh prepared by metal wire, wire diameter of 0.3-2.0mm metal wire. Hexagonal mesh is a good choice for breeding cage, he is through hot dip galvanized or PVC coated plastic disposal, the structure is tightly combined with no bump and convex appearance. Keep chickens and ducks, isolate chicken and duck houses, and try to take care of poultry.