The technical term “galvanizing” means that the metal has been specially treated with zinc. Essentially, it’s wire covered with a very thin layer of zinc. It is because of this thin layer of zinc that galvanized wire has many characteristics. Zinc can be galvanized by dipping the wire into a zinc bath or by electroplating.

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

As we all know, the mechanism of resistance to atmospheric corrosion of zinc includes mechanical protection and electrochemical protection. Under the condition of atmospheric corrosion, there are ZnO, Zn(OH)2 and basic zinc carbonate protective film on the surface of zinc layer, which to a certain extent slows the corrosion of zinc. When this protective film (also known as white rust) is damaged, a new film will be formed.

Hexagon mesh weight calculation method is: hexagon mesh weight calculation method: wire.× wire.× base x length x width ÷2=kg base: 1/2′=2.151′=1.273/4′=1.65/8′=1.875/4′=1.091′x1/2′ : 3′=0.4 warp.× Warp.×2x length x width ÷8×3=kg

The main raw materials of blade barbed wire are galvanized wire and galvanized sheet. Because the price of galvanized sheet is more expensive than galvanized wire, it is directly reflected in the price of blade barbed wire. There is also the difference in processing technology also leads to the difference in the price of the blade. The traditional barbed rope is made of mechanical wringing, which has a relatively small amount of labor and high production efficiency. However, the blade barbed rope is processed manually after secondary mechanical processing. So whether from the labor force or from the production efficiency also said that there is a large gap. These factors lead to the price of the blade barbed rope is more expensive.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.