Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.

Poor pretreatment before plating; Bath temperature is too low; Poor quality of additives or too many additives and organic impurities will cause poor bonding. The quality of additives also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the crystal lattice and cause stress, causing the coating to bubble.

The diameter of cold-drawn wire should conform to the contract, check whether the amount of zinc meets the requirements of the contract, check the tensile strength, and ask the factory to provide the corresponding inspection report. The wire factory introduces that the weight of a single coil of wire of different specifications should not be lower than the volume weight required by the contract, and record the value. No contacts are generated for each reel of wire. If there are contacts, no more than three contacts are generated for each reel. Each contact should be smooth surface treatment, the wire can not be pulled off from the contact, in line with customer packaging requirements.

Stainless steel blade barbed rope production process is basically similar to galvanized blade barbed rope production process, usually according to the mold to determine the size of the blade.