Stainless steel blade barbed rope under normal circumstances, basically 20 or 30 years is no problem, but because of the problem of its own material will appear a certain degree of rust, this is also because usually stainless steel blade barbed rope used by the material is 304 material, in daily use if in a long-term humid environment will cause certain corrosion. But usually users buy stainless steel blade barbed rope is basically life will not have problems users can also rest assured to use.

After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.

Stainless steel hexagonal network is composed of machine will be produced stainless steel wire of a kind of metal mesh, not easy corrosion, the survival of the fixed number of year is longer, net of wide, coarser size, strong practicability, flexibility and other unique places, stainless steel hexagonal wire netting material is stainless steel wire, wire diameter because stainless steel wire big viscosity of large stainless steel hexagonal network would be hard to manufacture, Of course, it is more difficult to hold the edge or twist the edge, so stainless steel hexagonal mesh whether from the material or artificial are expensive, but stainless steel hexagonal mesh will not rust and use years is also very long, appearance without disposal can achieve the use effect.

In the purchase of large rolls of galvanized wire, see the hardness of galvanized wire first, only after the hardness reaches the standard can be used. The hardness standard of large roll galvanized wire is a very important performance index and an economic test method. But for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

Dog cage mainly by welding, spraying, injection molding, surface treatment, electroplating dog cage is made of high quality steel wire, dog cages are with plastic and plastic surface treatment, electrophoresis, chrome plating, galvanized, imitation gold, etc., according to the customer request processing, respectively, also can be customized to sample, dog cage assembly of compact structure, neat and beautiful appearance, make folding and remove the cage is more convenient and quick, won’t take up too much space.

Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

Now most people buy barbed rope choose blade barbed rope, why is this? The blade gill net is made of hot-dip galvanized steel plate or stainless steel sheet to punch out sharp knife sheets. The high tension galvanized steel wire or blade barbed wire is made of stainless steel wire as the core wire. Because the gill net shape is not easy to contact, so it can reach excellent protection barrier effect. The primary raw materials of the product are galvanized sheet and stainless steel plate.

Barbed rope is an isolation protective net made of iron wire, which is wound on the main line (twisted wire) through the winding machine and through various weaving processes. Thorn rope generally has three methods of twisting, the following Haorong for you to introduce in detail.

Raw material of wire mesh sheet cold drawn low carbon steel wire base material can choose low carbon steel hot rolled disk bar or hot rolled smooth steel bar. The base material number and diameter of cold-drawn low carbon steel wire can be confirmed according to the rules in the table below. During the cold drawing process, the surface shrinkage rate of each drawing should not be greater than the wire mesh before cold drawing. Annealing shall not be carried out during wire drawing. If butt welding is required, the same production unit and base material of the same number should be selected. The appearance quality of wire mesh should not affect wire drawing. When the welding function is poor or brittle fracture occurs, special inspection should be carried out according to relevant standards.