The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

Welding mesh is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal fences, flower fences, window fences, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative. We can make it according to the special requirements of customers. Welding mesh is made of high quality low carbon steel wire row welding, and then cold plating (electroplating), hot plating, PVC plastic coated surface passivation, plasticizing treatment, smooth mesh, uniform mesh, solid solder joint, local machining stable performance, corrosion resistance, corrosion resistance. Features: Stainless steel mesh selection of high quality stainless steel wire row welding, more acid, alkali resistance, solid welding, beautiful, widely used and so on.

Hot dip galvanizing is then oiled and chromed. The quality of hot-galvanized sheet produced by this method is significantly improved compared with that by wet galvanizing method. It is only valuable for small-scale production. Continuous galvanizing production line includes a series of pretreatment procedures, such as alkali degreasing, hydrochloric acid pickling, water washing, solvent coating, drying, etc., and the original plate needs to be annealed in cover furnace before entering the galvanizing line.

Large rolls of galvanized wire in oxygen violently extinguished, spark, and sodium block, magnesium strip in oxygen extinguished, no spark phenomenon. This phenomenon is determined by the composition of galvanized wire. The galvanized wire used in the experiment is pig iron or steel wire, pig iron and steel are iron and carbon alloy, containing iron and carbon two elements of complex material. Carbon in galvanized wire will produce carbon dioxide when extinguished, solid into gas, volume will shrink rapidly.

The more turns thorn rope, at the same time will shorten some use the length, but its tensile strength is improved and barbed wire manufacturer production products general laps for the 3 ring, very few customers to use the product requires 5 laps, this time both in processing fees and use the length is calculated need extra.