Electric galvanized wire direct selling is in the plating tank through the current one-way to gradually zinc plating on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

Packaging: electric welding net general packaging for moisture-proof paper (color is mostly gray white, yellow, plus trademarks, certificates, etc.), some like 0.3-0.6mm domestic sales of small wire diameter electric welding net, because the wire is relatively soft, coupled with small volume, customers often require packing processing, in order to prevent shipment caused by damage. The wire of electric welding mesh has straight, also has a wavy bend (also known as the Dutch net).

Razor wire, also known as razor wire and razor net, is a new type of protective net. Blade barbed rope has beautiful, economical and practical, good resistance effect, convenient construction and other excellent characteristics.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

We basically know that the barbed wire fence generally has two kinds of ring and linear filamentous, the overall protective wire mesh selection of galvanized, stainless steel processing raw materials, long-term use is not easy to rust. Barbed wire fence uses stainless steel barbed wire, plastic coated barbed wire, aluminum coated barbed wire, galvanized barbed wire and other raw materials through special wire drawing into the strand planning, has a strong role in protection and maintenance. Widely used on both sides of the highway, grassland, gardens and other places, because it is a field protection product and therefore updated faster, so how to use the barbed wire fence after abandonment? Here are some of the uses of discarded blades.

The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.