3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

Widely used in practice, iron wire also has certain harm, simple rust and corrosion, so we can generally use galvanized method to prevent product corrosion. Together in addition to this method, metal commonly used treatment methods and phosphating treatment, oxidation treatment, etc. Metal phosphating treatment: iron and steel products to remove oil, rust, into the specific composition of the salt solution soak, you can form a layer of water soluble salt film on the surface of the metal, this process is called phosphating treatment.

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

The wire used for wire mesh is made of low carbon steel wire, medium carbon steel wire, high carbon steel wire, stainless steel wire and other materials woven or welded. Production technology: general braid, embossed braid and spot welding type. If the steel wire as the material, after the equipment processing into a network, so called wire mesh.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

Barbed rope is an isolation protective net made of iron wire, which is wound on the main line (twisted wire) through the winding machine and through various weaving processes. Thorn rope generally has three methods of twisting, the following Haorong for you to introduce in detail.

The advantages of hexagonal net to do jet hanging net, the first is that the processing speed is fast, the cost is low, and it is very good to roll out when it is open because of the edge. Common specifications: 12 cm x15 cm (11cm x11 cm) 11 cm x15 cm (10 cm x10 cm) 10 cm x12 cm (9 cm x9 cm) 9 cm x13 cm (9 cm x9 cm) 8 cm x10 cm (7 cm x7 cm) common wire: 1.3mm 1.4mm 1.5mm 1.6mm 1.7mm 1.8mm 2.0mm 2.3mm 2.5mm Commonly used materials: galvanized wire hot dip galvanized wire to wire drawn zinc aluminum alloy plastic coated wire stainless steel wire.

Hexagonal net value is quite high in landslides, many slope through the baptism of the rain after this, there may occur sediment flow of plague and as a result some losses to the property of the people, have the existence of hexagonal wire netting, can solve this problem, from the fundamental up sediment flow in came it can help guard against protection, achieve low is the loss of many people.

The protective duration of the galvanized layer of large roll galvanized wire is closely related to the thickness of the coating. Generally speaking, in relatively dry main gas and indoor use, and in harsh environmental conditions, the thickness of galvanized layer needs to be very high. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance.