In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

Cold wire drawing is a kind of cold processing of metal. The raw material is wire rod, which is produced by peeling, galvanizing and other processes. Galvanized cold drawing is used more in building materials. Its testing standards are also different. The strength of cold drawing is relatively high. Because of the high strength of steel, it plays a very important role in construction. It saves the construction steel in building materials, and also reduces the cost of the project. It also plays a very important role in the structure of concrete.

Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it is also necessary to conduct reasonable post-processing to avoid affecting its use effect. Of course, when the black iron wire is galvanized, it is also necessary to ensure the thickness of the galvanized layer, so that it can also reduce the possibility of rust. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

Every galvanized wire production into the peak season of the industry, the road to the factory will from time to time see transportation wire and container container vehicles, as well as galvanized bright silk short-distance transportation trucks, led to the utilization of labor in the surrounding countryside, solved the employment problem of most people. Galvanized wire is divided into hot plating wire and cold plating wire.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.