Steel wire and iron wire have many similarities, but carefully distinguish, will find that they are not only different in the material, but also in the product characteristics of the great difference. So when choosing, be sure to make a clear distinction between the two. Steel wire factory introduces steel wire carbon structural steel made above, generally not galvanized, used for machinery, spring. Black, very hard; Wire: made of mild steel (mild steel), galvanized, used for joining and binding. White and soft.

Because the coating obtained is thicker, hot-dip galvanizing has very good protective function than electric galvanizing, so it is an important maintenance coating for iron and steel parts in strict working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding and other occupations. In the field of agriculture, such as pesticide irrigation, greenhouse and construction industry such as water and gas transportation, wire casing, scaffolding, Bridges, highway guardrail and other aspects, it has been widely used in these years.

Greenhouse steel pipe is mainly made of greenhouse composite materials made of pull rod, pressure rod, column, and arch rod to cover the plastic film in a greenhouse. Wire factory introduces its this shape is circular plastic greenhouse, this greenhouse covers a large area, the effect of heat absorption is also very good, convenient to build, the cost of building a is also very low. The raw material source of greenhouse steel pipe is very rich and extensive, and the application effect is good.

There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.

In our daily life, what we can bend with our hands is basically galvanized iron wire, not steel wire. It has a high zinc content, which ensures excellent toughness and resilience, as well as ultra-high corrosion resistance, which can be maintained in outdoor environments for decades. There are many practical galvanized iron wire, such as strong reliability, galvanized layer and iron together, forming a special metallurgical structure, in the use and transportation process, can ensure that it will not be mechanical damage.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.

The invention technology is used to put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and plays an important measure to stabilize the PH value within a numerical range, and also facilitate the filter filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

In order to pack and bundle galvanized wire on the surface of the deposit layer to remove the surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is caused by soaps and saponable fatty surfactants being brought into the tank. Moderate foam formation rates may be harmless. Small homogeneous particles of large denier present in the tank can stabilize the foam layer. To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the intake of surfactant. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.