There are two varieties of steel grid plate is pressure welded steel grid plate and pressure lock steel grid plate, in many people’s eyes, these two products belong to the same variety, in fact, there are still great differences between them in many places.

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.

Traditional barbed wire is crisscross woven into the wire, with the development of the economy, the rapid rise of all walks of life, the limitations of the use of traditional barbed wire gradually exposed, such as: aquaculture, to the chicken circle cage can not be too dense, the wire can not be too thick, woven mesh wire once the mesh will become soft. We also have coping methods: 1, cotton gouging, rolling straight wire into wavy shape, but still not enough to raise chickens with mesh can only be extended to the beak can not feed! 2, is the electric welding net, with the current of the longitude and weft wire spot welding together, the mesh is not limited to do more.

2. The cleaning agent used for cleaning should have no effect on the binding force of the coating and no corrosion on the matrix.

Generally, due to wet weather and more precipitation, oxidation and rust of binding iron wire NetEase occurs, so we should better store and use galvanized iron wire to avoid rust as far as possible. About the barbed wire, the surface of the barbed wire attached a layer of galvanized layer, the galvanized layer if too thick will not meet the SGS environmental standards. But if it is too thin, it is easy to oxidize with water molecules and rust.

Zinc is a silver-white metal, brittle at room temperature, soluble in acid can also be soluble in alkali, known as amphoteric metal. Pure zinc in dry air is more stable, in humid air or containing carbon dioxide and oxygen water is small, the surface will generate a layer of basic zinc carbonate based thin film layer, it can delay the corrosion rate of zinc layer. The corrosion resistance of zinc coating in aqueous solution of acid, alkali and sodium chloride is stronger.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.