Galvanized iron wire is selected from excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

Surface coating, surface inclusion and other defects can be removed locally from the surface of the deposited layer before galvanized, which can be found and treated by conventional techniques. Excess foam is caused by the introduction of soap and saponable fatty surfactants into the tank. Moderate foam formation rates may be harmless. The presence of a large number of tiny homogenous particles in the tank, which can stabilize the foam layer, mat with activated carbon to remove surface active substances, or make the foam less stable through filtration, are effective measures.

The common weight standard of galvanized barbed rope is 25kg per coil, and the length of each coil varies from 220-250 meters according to the specifications of the barbed rope. And of course we all know that the heavier the disc the longer it is. But there is one point that is worth our attention, that is, the hollow inside the general larger disk is relatively small, and the hollow inside the lighter galvanized thorn rope is relatively large. The purpose of this is to reduce the number of bending of the thorn rope and make it easier and more beautiful when installing, on the other hand, it looks larger in appearance.

Hot wire is made of high quality low carbon steel, high carbon steel, after drawing, hot galvanized processing galvanized wire. Hot dip galvanized wire production process: wire rod – drawing – annealing – drawing – annealing – galvanized. Hot dip galvanized wire has the characteristics of thick coating, strong corrosion resistance and solid coating. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire. Hot-dip galvanized wire is of better quality than electrodip galvanized wire. In the production process, hot dip galvanized wire has more than one annealing process, so the corrosion resistance of hot dip galvanized wire is stronger than that of electric galvanized wire.