Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.

Galvanized hook mesh selection of low carbon steel wire, the surface of cold galvanized or hot galvanized anticorrosive treatment, strong mesh, strong protection, long anticorrosive time. Galvanized wire hook nets are widely used, widely used in warehouses, refrigeration between things, protective reinforcement, parks, zoos, Marine fishing fences and construction site fences, mechanical equipment protection.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

Generally, the main reasons for the rust of iron wire are: when the steel mesh in the metal mesh appears some dust, this time you can use some water or alkaline solution cleaning. Followed by floating iron or embedded iron, iron will rust, connected to the stainless steel plate mesh of iron rust, so these iron must be dealt with, can use carbon steel wire brush can also be used for processing carbon steel and so on. Then is the scratch, for the scratch, mainly in the production process, need some stubborn iron scratch stainless steel plate net special polishing cleaning machine.