Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

Unless the stainless steel blade barbed rope is specially customized, it is usually produced by the mould with the knife length of 22mm, which is the BTO-22 type we usually call. This is not necessarily the specification from 11mm to 65mm are specifications. Unless the customer insists on customized length requirements, the barbed rope manufacturer will produce BTO-22 stainless steel blade barbed rope.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.

As we all know, even if it is the same kind of steel wire, because of the steel making process, wire drawing process and equipment are not the same, so the quality of steel wire production is not the same. Due to the different mechanical properties of steel wire itself, flattening process and equipment, the width and elongation of steel wire in the flattening process have different effects. Therefore, in the selection of wire diameter, the following three factors should be considered:

The lighting surface of each type of shed is designed to be curved, improving the Angle of the light surface, because the lighting surface is curved, no dust accumulation, good light transmittance, high temperature in the shed, after measurement, the average temperature in the shed is 3℃ higher than the traditional bamboo pole cement column shed, the yield is increased by 15~20%, and the harvest date is advanced. The formula is scientific, the surface does not absorb moisture, do not return halogen through modification technology and scientific production process, solve the greenhouse frame rod is easy to absorb moisture return halogen, poor water resistance and easy to change the shortcomings, so that the greenhouse steel pipe in the high temperature and high humidity environment, few drops, frost phenomenon, and reduce pests and diseases.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.

Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.