After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

Hot dip galvanized wire is used in carbon structural steel, which is processed by drawing and hot dip galvanized. It is widely used in the manufacture of wire mesh, highway guardrail and construction projects. Electro galvanized wire is a kind of metal conforming material made of low carbon steel as core wire by wire drawing and electro galvanized process. Mainly used in wire mesh, highway guardrail and construction projects.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.

Compared with electric galvanized iron wire, hot dip galvanized iron wire has higher zinc layer, better anti-corrosion performance, and is suitable for the more important anti-corrosion and anti-rust status.

The construction of inner wall and outer wall steel wire mesh can effectively solve the wall cracks, falling off, empty drum phenomenon. Hot dip galvanized steel wire mesh material requirements: net surface leveling, width and length to meet the project required standards, welding process, weight, zinc, etc., with more production and operation, detection certificate is complete.