The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.

Hot drawing is the heating before the wire enters the die hole, mainly used for high melting point wire drawing; The temperature drawing is carried out by heating the heater to the range of temperature, mainly used for galvanized steel wire, difficult to deform drawing.

Now the production of stainless steel blade barbed rope unless it is a specially customized model, under normal circumstances are the use of a knife length of 22mm mold production, that is, we usually say bto-22 type. It’s not necessarily the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the required length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

2, galvanized wire mesh molding sheet storage ground should be flat, according to the symbolic requirements of the accumulation of regular, height should not exceed 2M, and away from heat sources, avoid exposure.